Maxxam™ PP5120R B2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | khtxmY_Maxxam-PP5120R-B2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 to 22 | g/10 min | ISO 1133 |
| Molding Shrinkage (3.20 mm) | 1.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 27.0 | MPa | ISO 527 |
| Tensile Strain (Break) | 16 | % | ISO 527-2 |
| Flexural Modulus 2 | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 1.2 | kJ/m² | |
| 23°C | 2.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 63.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | ISO 3795 |
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 185 to 200 | °C | |
| Middle Temperature | 200 to 215 | °C | |
| Front Temperature | 205 to 220 | °C | |
| Nozzle Temperature | 205 to 220 | °C | |
| Mold Temperature | 40.0 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 8.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan A-9190/B-8290 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| KEP® 7141 | Kumho Polychem Co., Ltd. | EPDM | KEP® |
| Kynar Flex® 2800 WR | Arkema | PVDF | Kynar Flex® |
| INLUBE PPSTF18SI2 | Infinity LTL Engineered Compounds | PPS | INLUBE |
| Sylvin 2981-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |