| DIALAC® TW21H is a Styrene Acrylonitrile Silicone Copolymer (SAS) material. It is available in Asia Pacific or North America for injection molding. Primary attribute of DIALAC® TW21H: RoHS Compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 2.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 102 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 43.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 1950 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 93.0 | °C | ISO 75-2/Af |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 210 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0436C30L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| BMC 615 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Europrene® SOL T 172 | Versalis S.p.A. | SBS | Europrene® |
| Exelene® LDPE 0700 | Montachem International, Inc. | LDPE | Exelene® LDPE |
| LNP™ STAT-KON™ QD000I compound | SABIC Innovative Plastics | Nylon 610 | LNP™ STAT-KON™ |