HiFill® PA4/6 GF40 HS
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgW0Gr_HiFill-PA4-6-GF40-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA4/6 GF40 HS is a Polyamide 46 (Nylon 46) product filled with 40% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 228 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 317 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| CLTE - Flow | 3.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 22 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| TPCI # | 9627150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 282 to 316 | °C | |
| Middle Temperature | 282 to 316 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Processing (Melt) Temp | 246 to 316 | °C | |
| Mold Temperature | 87.8 to 127 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9035 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| TES J-1200/30/VO/Natl | Techmer Engineered Solutions | ABS | TES |
| VITAMIDE® AS10NT6050 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Sylvin 9812-80C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ KL001 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |