ARCEL® 730B (2.50 pcf)
| Category: | PS+PE , Polystyrene + PE |
| Manufacturer: | NOVA Chemicals |
| Trademark: | ARCEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgR6EG_ARCEL-730B-2-50-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ARCEL® 730B (2.50 pcf) is a Polystyrene + PE (PS+PE) material. It is available in North America for foam processing. Typical application of ARCEL® 730B (2.50 pcf): Foam |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.0400 | g/cm³ | ASTM D3575 |
| Particle Size - 98% | 0.800 to 1.70 | mm | |
| VOC Content | |||
| Pentane | 11 | % | |
| Plasticizer | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain | 10 | % | ASTM C203 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength - at Maximum Load | 3.2 | kN/m | ASTM D3575 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 0.542 | MPa | ASTM D3575 |
| Flexural Strength | ASTM C203 | ||
| -- | 0.534 | MPa | |
| 5.0% Strain | 0.479 | MPa | |
| Compressive Strength | ASTM D3575 | ||
| 10% Strain | 0.238 | MPa | |
| 25% Strain | 0.276 | MPa | |
| 50% Strain | 0.345 | MPa | |
| 75% Strain | 0.690 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC G-95-064A | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| VITAMIDE® AT37NT6314 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Unipren® Elastomers A3 CRLA010 45A EB05IN1 UP358 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Karina MBU BROWN E 3600/004-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® B 2505 000000 | LANXESS GmbH | PBT | POCAN® |