RTP 1400 R-5800
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgQNkE_RTP-1400-R-5800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Flow |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (365°C/5.0 kg) | 22 - 28 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.37 | % | ASTM D570 |
| Moisture Content | 0.040 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength | 69.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 90 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 209 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+12 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 343 - 388 | °C | |
| Mold Temperature | 138 - 163 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® M-56 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| SLOVASTER® B FRN 3 LS | Plastcom | PBT | SLOVASTER® |
| FHR EPS R-MER II® 5627 (1.75 lb/ft³) | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| LNP™ THERMOCOMP™ DF008 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Polifil® PP C-10 | The Plastics Group | PP Homopolymer | Polifil® PP |