Category:	EMAA , Ethylene Methacrylic Acid
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS EMAA
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kfOtst_INEOS-EMAA-M21N430.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Benefits & Features
M21N430 is an additive free ethylene-methacrylic-acid-copolymer (EMAA) with a low MAA content. Its special polymer structure gives the following properties:

Improved adhesion properties to standard LDPE/mLLDPE or other polar substrates, especially with aluminium foil and metallised film at high line speeds or low coating weights

Good processability in mono- and coextrusion with comparable neck-in and draw down to LDPE

Exhibits good sealing properties enhanced by the presence of the comonomer

Good organoleptical properties

Low fumes during processing, high purity and a low gel level

Applications
M21N430 is a speciality extrusion coating resin with improved adhesion characteristics. Main application fields include aluminium foil and metallized film coating both for industrial use, food and flexible packaging.

General Information
Features	Additive Free Copolymer Good Adhesion Good Heat Seal Good Organoleptic Properties Good Processability High Purity Low Gel Low to No Fumes
Uses	Coating Applications Foil Coatings Food Packaging Industrial Applications Packaging
RoHS Compliance	Contact Manufacturer
Forms	Pellets
Processing Method	Coextrusion Extrusion Coating

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.5	g/10 min	ISO 1133
Methacrylic Acid Content	1.2	%	Internal Method

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, Compression Molded)	48		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress			ISO 527-2
Yield, Compression Molded	9.00	MPa
Break, Compression Molded	10.5	MPa
Tensile Strain (Break, Compression Molded)	500	%	ISO 527-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	90.0	°C	ISO 306/A50
Melting Temperature (DSC) ¹	108	°C	Internal Method

Extrusion	Nominal Value	Unit
Melt Temperature	260 to 325	°C

Note Message
1 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
THERMORUN® 215B	Mitsubishi Chemical Performance Polymers, Inc.	TPE	THERMORUN®
DELPET™ FILB72	Asahi Kasei Chemicals Corporation	Acrylic (PMMA)	DELPET™
Ferro PP LPP20BN40BK	Ferro Corporation	PP, Unspecified	Ferro PP
Iupital® F40-03	Mitsubishi Engineering-Plastics Corp	Acetal (POM) Copolymer	Iupital®
Pearlbond™ 12C75	Lubrizol Advanced Materials, Inc.	TPU-Polyester	Pearlbond™