Sumikon® PM-3050
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kf92q3_SumikonPM3050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-3050 (Type J Black) is Glass fiber, Inorganic filler and Organic fiber filled novolac resin molding compound with good mechanical property. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.26 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.12 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 117 | MPa | JIS K6911 |
| Flexural Modulus | 12900 | MPa | JIS K6911 |
| Flexural Strength | 197 | MPa | JIS K6911 |
| Compressive Strength | 251 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.2 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 16 | kV/mm | JIS K6911 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 4.0E+11 | ohms | JIS K6911 |
| -- 3 | 5.0E+10 | ohms | JIS K6911 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA66 6G/3L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| APEX® 13-A4448A-119NT | Teknor Apex Company | PVC, Rigid | APEX® |
| Extir® LN 3000 | Versalis S.p.A. | PS (EPS) | Extir® |
| HAIPLEN EP10 G2 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| PERLEX® R5550 | A. Schulman Europe | PC | PERLEX® |