KRALASTIC® SR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | KRALASTIC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kesCUe_KRALASTIC-SR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KRALASTIC®SR is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is extrusion. KRALASTIC®The main characteristics of SR are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 2.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.60 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 104 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 44.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 8.6E-5 | cm/cm/°C | JIS K7197 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Ball Pressure Registration Temperature: 90°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | > 3.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN SFC-650BT | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| TRANSMARE® 12CT20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Kumho ABS 780 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| SCHULARENE™ N3102 | A. Schulman Europe | PLA | SCHULARENE™ |
| LUVOCOM® 3-8896/WT/V-0 | LEHVOSS Group | Nylon 6 | LUVOCOM® |