EMERGE™ PC 8310-10 (AP)
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | keUF8T_EMERGE-PC-8310-10-AP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE* PC 8310-10 advanced resin is a transparent and ignition resistant PC resin that contains no chlorinated or brominated nor phosphorous-based additives. It is a transparent material with UL-94 V-0 rating at 2.5 mm. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2400 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 60.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 66.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 6.0 | % | |
| Break, 3.20 mm, Injection Molded | 120 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2400 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Compression Molded) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 900 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 128 | °C | |
| 1.8 MPa, Annealed | 142 | °C | |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 1 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.50 mm | V-2 | ||
| 2.50 mm | V-0 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 84.0 to 87.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 503 TFE 10 | RTP Company | SAN | RTP |
| Next Nylon 6 Industrial Series NG35-02BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Industrial Series |
| DuClear® QU 80 A | Ducor Petrochemicals BV | PP Random Copolymer | DuClear® |
| POLYfill PPH TS5040DS | Polykemi AB | PP Homopolymer | POLYfill |
| SIBUR Synthetic Rubber SSBR-2560 TDAE Grade D | SIBUR | SBR, Solution | SIBUR Synthetic Rubber |