Bayblend® W90 XG
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ke2Hpf_BayblendW90XG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ASA-Blend; Vicat/B 120 temperature = 115°C; UV-stabilized; very good surface finish |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 34.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Transverse flow : 2.00mm | 0.50 - 0.70 | % | ISO 2577 |
| Flow : 2.00mm | 0.50 - 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2830 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 65.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.0 | % | ISO 527-2/50 |
| Fracture, 23°C | 50 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2840 | MPa | ISO 178 |
| Flexural Stress 3(3.5% Strain, 23°C) | 85.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 4(23°C) | 5.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/A |
| 23°C | 14 | kJ/m² | ISO 180/A |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 20.0 | J | ISO 6603-2 |
| 23°C | 45.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 4250 | N | ISO 6603-2 |
| 23°C | 4800 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ISO 306/B50 |
| -- | 115 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 60x60x2 mm |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miraprene® QS2217 | Mitsubishi Chemical Corporation | TPO (POE) | Miraprene® |
| Torlon® AI-30 LM | Solvay Specialty Polymers | PAI | Torlon® |
| ESTOPLAST EP 4020 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| O'Tech OW 836 FR | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Sylvin 9710-80FUV Orange 574 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |