Generic Phenolic - Mineral
| Category: | Phenolic , Phenolic |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kdyYdr_Generic-Phenolic---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Phenolic - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.46 - 1.89 | g/cm³ | ASTM D792 |
| 23°C | 1.49 - 1.59 | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 - 0.88 | g/cm³ | ASTM D1895 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.13 - 0.64 | % | ASTM D955 |
| 23°C | 0.41 - 0.75 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.040 - 0.54 | % | ASTM D570 |
| 23°C, 24 hr | 0.020 - 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 57 - 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8300 - 17200 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 31.0 - 60.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 0.30 - 0.81 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7380 - 9910 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23°C | 59.0 - 175 | MPa | ASTM D790 |
| 23°C | 75.0 - 165 | MPa | ISO 178 |
| Compressive Strength (23°C) | 138 - 243 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14.4 - 25.3 | J/m | ASTM D256 |
| Notched Izod Impact (23°C) | 15 - 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 167 - 207 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 155 - 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 195 - 218 | °C | ASTM D794 |
| CLTE - Flow | 1.4E-5 - 5.8E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 150 - 180 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 2.1E+9 - 1.2E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | |||
| 23°C | 7.4 - 18 | kV/mm | ASTM D149 |
| 23°C | 6.0 - 39 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 4.66 - 6.09 | ASTM D150 | |
| 23°C | 4.30 - 5.50 | ASTM D2520 | |
| Dissipation Factor (23°C) | 5.3E-3 - 0.076 | ASTM D150 | |
| Arc Resistance | 155 - 186 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 173 - 176 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 26 - 38 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 - 74.4 | °C | |
| Middle Temperature | 65.0 - 74.1 | °C | |
| Front Temperature | 89.9 - 90.5 | °C | |
| Nozzle Temperature | 87.8 - 95.0 | °C | |
| Processing (Melt) Temp | 107 - 110 | °C | |
| Mold Temperature | 174 | °C | |
| Injection Pressure | 8.60 - 175 | MPa | |
| Back Pressure | 0.207 - 0.452 | MPa | |
| Screw Speed | 60 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Phenolic - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-313 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Niplene F40 AGR | Soredi S.p.a. | PP Homopolymer | Niplene |
| ALCOM® PC 740/4 UV WT1257-04LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| KOCETAL® GB705 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| OxyVinyls® 225P | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |