LubriOne™ MP-20GF/15T BLACK
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kdvUUw_LubriOne-MP-20GF-15T-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5850 | MPa | ASTM D638 |
| Tensile Strength 2 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 4 | 6050 | MPa | ASTM D790 |
| Flexural Strength 5 | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 135 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 270 - 300 | °C | |
| Mold Temperature | 65.0 - 95.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 1808AF00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| MIRASON™ 16SPO | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| RJM SN602-NH | RJM International, Inc. | Nylon 66 | RJM |
| Spartech Polycom SC21-1093U | Spartech Polycom | PBT | Spartech |
| Tufel® II 94605 | Momentive Performance Materials Inc. | Silicone | Tufel® II |