Tarnamid® T-27 MCS V2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kdRUTz_Tarnamid-T-27-MCS-V2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tarnamid®T-27 MCS V2 is a polyamide 6 (nylon 6) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Tarnamid®The main features of T-27 MCS V2 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/5.0 kg) | 140 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 | 1.3 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.5 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 150 | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3600 | 1800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | -- | % | ISO 527-2 |
| Flexural Stress | 95.0 | 30.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 80 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | 180 | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Glow Wire Resistance, PN-EN-60695-2-1, 2mm: 850Note: All electrical properties were tested in accordance with the IEC test standard.Comparative Track Index, IEC 112, Solution A: 600 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 130 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 50YM240 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Westlake LDPE EF601 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Dugdale PVC Lead Free Purge Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| Alathon® L4930TC | LyondellBasell Industries | HDPE | Alathon® |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |