VALOX™ 337 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kd6FcC_VALOX-337-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low temperature impact PBT. Automotive applications: underhood power distribution boxes and covers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 2.4 to 2.7 | % | |
| Across Flow : 3.20 mm | 2.4 to 2.7 | % | |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 39.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 3.9 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 1790 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 56.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 800 | J/m | |
| 23°C | 870 | J/m | |
| Unnotched Izod Impact | ASTM D4812 | ||
| -30°C | 3200 | J/m | |
| 23°C | 3200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 98.9 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 47.2 | °C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 1250 | Pa·s | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Nozzle Temperature | 238 to 254 | °C | |
| Processing (Melt) Temp | 243 to 260 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® HTplus F1001 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| Fiberfil® J-69/30/E/M | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Ducor® DE1040U | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| ICORENE® N2104 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |
| Rotuba CAB B900 (13% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |