Radilon® S LVHPL128 100 NAT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kbzq4x_Radilon-S-LVHPL128-100-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 low viscosity injection moulding grade. Plasticized. Natural colour. Suitable for parts requiring very high flexibility and elongation at break. ISO 1043 : PA6-P |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 6.6 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1000 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 45.0 | -- | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 40 | -- | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 100 | -- | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 30.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 18 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 150 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 165 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 215 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 30 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP1B20 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Retpol® 3053 HS UV3 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Starex WX-9700 | SAMSUNG SDI CO., LTD. | ASA | Starex |
| APEX® 3701-75NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Petrothene® LP540200X03 | LyondellBasell Industries | HDPE | Petrothene® |