ResMart Plus Nylon 6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | ResMart |
| Trademark: | ResMart Plus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kbSdUp_ResMart-Plus-Nylon-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General purpose nylon 6 that displays excellent colorability and property set |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 171 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 82.2 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 243 - 279 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Dew Point: 0°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 10 TFE 10 | RTP Company | Nylon 66 | RTP |
| Propilven J-400 | Propilven, S.A. | PP, Unspecified | Propilven |
| NAXALOY® 770-NT137 | MRC Polymers, Inc. | PC+ABS | NAXALOY® |
| APEX® RE 8103R-NT | Teknor Apex Company | PVC, Rigid | APEX® |
| COBITECH 2 | M&G Gruppo Mossi & Ghisolfi | PET | COBITECH |