Eltex® PF1315AZ
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kaZsfX_EltexPF1315AZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Additive free C6 m-LLDPE for extrusion coating, injection moulding and compounding. Benefits & Features
Applications For extrusion coating:
For injection moulding and compounding:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.914 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (Compression Molded) | 175 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 217 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C, Compression Molded) | 9.00 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, molding | 22 | % | ISO 527-2 |
| Fracture, molding | > 600 | % | ISO 527-2 |
| Flexural Modulus (23°C, Compression Molded) | 244 | MPa | ISO 178 |
| Tensile fracture strength- Compression Molded | No Break | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat of Fusion | 104 | J/g | ASTM D3418 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-20°C, Compression Molded) | 71 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A50 |
| Melting Temperature 1 | 96.0 - 114 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 84 - 100 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | < 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 280 | °C |
| Note Message | |
|---|---|
| 1 . | DSC 2nd heating 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1521AH | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| TufCoat™ IDES 208539 | Lucite International Inc. | Acrylic (PMMA) | TufCoat™ |
| Dryflex® 4103 | ELASTO | TPE | Dryflex® |
| Electrafil® 02010 MB | Techmer Engineered Solutions | PP, Unspecified | Electrafil® |
| Sylvin 9788F1 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |