VALOX™ 771 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kaKqnz_VALOX-771-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% mineral/glass reinforced flame retardant grade with a CTI performance level class of 0 rating. Applications which may see electrical arcing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.65 to 0.85 | % | |
| Across Flow | 1.0 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 5860 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 217 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 196 | °C | |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance 6 | PLC 4 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.610 mm | V-2 | ||
| 0.760 mm | V-0 | ||
| 2.01 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 3.00 mm 7 | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 750 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 243 to 254 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 254 to 266 | °C | |
| Nozzle Temperature | 254 to 271 | °C | |
| Processing (Melt) Temp | 254 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Tungsten Electrode |
| 7 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-50/40/ NAT | Techmer Engineered Solutions | PC | TES |
| Wondel® P PR0M4 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| Hifax CA1147A | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| King Pearl® FD-A | Loyal Chemical | PS (EPS) | King Pearl® |
| LNP™ THERMOCOMP™ IX04513C compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |