PRL AH-GP1
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kZgPNz_PRL-AH-GP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL AH-GP1 is a polyoxymethylene (POM) homopolymer product,. It can be processed by extrusion or injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 1.0 - 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 - 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18mm | 67.6 | MPa | ASTM D638 |
| Fracture, 3.18mm | 67.6 | MPa | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2830 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 94.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 120 | J/m | ASTM D256 |
| Dart Drop Impact (3.18 mm) | 22.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 166 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 110 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 196 - 207 | °C | |
| Front Temperature | 199 - 210 | °C | |
| Processing (Melt) Temp | 199 - 210 | °C | |
| Mold Temperature | 79.4 - 98.9 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 196 - 207 | °C | |
| Cylinder Zone 3 Temp. | 199 - 210 | °C | |
| Melt Temperature | 193 - 210 | °C | |
| Die Temperature | 79.4 - 98.9 | °C |
| Extrusion instructions |
|---|
| Drying Temperature: do not exceed 8 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP265 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| TOPAS® 9903D-10 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Petrotene® PP A2 G20 T10 PRTA011 PH204 MSP | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Pexidan® R/T | Saco Polymers | XLPE | Pexidan® |
| apilon 52® TL 45 NS | API SpA | TPU-Polyether | apilon 52® |