OpteSTAT™ PA6,6 DP502
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OpteSTAT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kZ3fYQ_OpteSTAT-PA6-6-DP502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OpteSTAT™ compounds are Ovation Polymers' line of nano-compounds based on carbon nanotubes. Our proprietary dispersion technology debundles and disentangles carbon nanotubes without compromising their integrity. OpteSTAT™ compounds exhibit good conductivity at minimal nanotube loadings, achieving exceptional cleanliness and physical property retention. OpteSTAT™ PA66 DP502 is a nylon 6,6 based carbon nanotube compound. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 2800 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 23°C) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C) | 3.1 | % | ASTM D638 |
| Flexural Modulus 4(23°C, 50.0 mm Span) | 2900 | MPa | ASTM D790 |
| Flexural Strength 5(5.0% Strain, 23°C, 50.0 mm Span) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 51 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 6 | 1.0E+6 to 1.0E+7 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | On Molded Plaques |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AECHVO | Arkema | Nylon 12 | Rilsamid® |
| AMTOPP CC15 | Inteplast Group | PP, Unspecified | AMTOPP |
| Fluon® ETFE | Asahi Glass Co., Ltd. | ETFE | Fluon® |
| Globalene® 6181 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| OmniLon™ PA6/6 U IM8 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |