Loyblend® HA-1700
| Category: | ABS+Acrylic , Acrylonitrile Butadiene Styrene + Acrylic (PMMA) |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Loyblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kYOkIr_Loyblend-HA-1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Loyblend® HA-1700 is compounded blend of poly methyl methacrylate and acrylonitrile-butadiene-styrene. This grade offers high hardness, good scratch resistance and excellent weathering resistance with a good gloss surface |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2060 | MPa | ASTM D790 |
| Flexural Strength | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 86.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 195 to 205 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex WR-9140 | SAMSUNG SDI CO., LTD. | ASA | Starex |
| NYLEM® 6 GFR 15 IM | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| Daelim Po1y® LD-01 | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| Elastane™ 4725-85A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Karina IVORY PVC COMPOUND 850-35/1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |