NEFTEKHIM ABS 1534
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kXtAxR_NEFTEKHIM-ABS-1534.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS 1534 - is an easy flow, molding grade with a good heat resistance during the process. It is used for production of household appliances, particularly, for complicated parts closed to heat source (front panel, washing machine frame). It is used for production of electrical goods as well. This grade is produced self-colored only, additives/dye free |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 12 to 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 2350 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | DIN 53453 |
| Notched Izod Impact Strength (23°C) | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Deflection Temperature | 102 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Styrene 2 | 0.050 | % | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-1 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (20°) | 50 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | Test Method: TU 2214-159-05766801-2011 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROTEK® PK-VM natural (4774) | AKRO-PLASTIC GmbH | PK-Aliphatic | AKROTEK® |
| Fluon® PTFE RB1020S | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| ESENTTIA 01C27NT-T | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| LEXAN™ EXL1112 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| KEBAFORM® C 901 CB | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |