InnoTuf® TP-4004
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kXhvKP_InnoTuf-TP-4004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4004 is an impact resistant polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained without the utilization of mercuiy, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Base Resin | 1.16 | g/cm³ | |
| Cured | 1.17 | g/cm³ | |
| Hardener | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 586 | MPa | ASTM D790 |
| Flexural Strength | 27.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 100 | °C | |
| 1.8 MPa, Unannealed | 83.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 48 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time (66°C) | 60 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.10 | Pa·s | |
| 38°C 2 | 2.1 | Pa·s | |
| 38°C 3 | 5.1 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 10 to 14 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 to 70 | ASTM D2240 | |
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Tensile Elongation at Break | 70 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 1 hour at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6431 | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| Sylvin 7841-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| WPP PP PPC2935-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| YUNTIANHUA® EF | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| Asaflex™ 805 | AKelastomers | SBS | Asaflex™ |