Edgetek™ NN-50GF/000EM L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kXM99Z_Edgetek-NN-50GF-000EM-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Edgetek™ NN-50GF/000EM L is a Polyamide 66 (Nylon 66) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 16500 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 224 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 15200 | MPa | ASTM D790 |
| Flexural Strength | 317 | MPa | ASTM D790 |
| Compressive Strength | 185 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 3.18 mm | 254 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 254 | °C | |
| CLTE - Flow | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.53 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 282 to 299 | °C | |
| Mold Temperature | 87.8 to 107 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 387 FR | RTP Company | PC | RTP |
| Torayca® ASHT-18A | Toray Resin Company | ABS | Torayca® |
| CALP HG2310A | Lion Idemitsu Composites Co., Ltd. | Nylon, Unspecified | CALP |
| DOMAMID® 6G30 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| EPO-TEK® EK1000-1 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |