VYPET VNT 630
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kX0kZ0_VYPET-VNT-630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vypet 630 is a 30 % glass reinforced PET injection molding compound designed for electrical and structural applications. Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.56 | g/cm³ | ASTM D792 |
| 23°C | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 2.00mm | 0.40 | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.80 | % | ASTM D955 |
| Vertical flow direction : 2.00mm | 0.80 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.40 | % | ISO 294-4 |
| Ash Content | |||
| -- | 30 | % | ASTM D2854 |
| -- | 30 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 145 | MPa | ASTM D638 |
| Yield | 140 | MPa | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 9200 | MPa | ASTM D790 |
| -- 3 | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 210 | MPa | ASTM D790 |
| -- 5 | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 225 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 270 - 295 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Processing (Melt) Temp | 275 - 300 | °C | |
| Mold Temperature | 95.0 - 120 | °C | |
| Injection Pressure | 55.0 - 85.0 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 75 | rpm |
| Injection instructions |
|---|
| Back Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4001G15 | POLYROCKS CHEMICAL CO., LTD | Nylon 66 | PONYL |
| Unichem 4160C | Colorite Polymers | PVC, Unspecified | Unichem |
| EVICOM™ RI5/020 | INEOS Compounds | PVC, Rigid | EVICOM™ |
| FRblend® PA6-1302 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | FRblend® |
| MARPOL® mLLF 801-CSB | Marco Polo International, Inc. | mLLDPE | MARPOL® |