PENTALLOY BS 6 H natur
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTALLOY BS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kWzDhe_PENTALLOY-BS-6-H-natur.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA-ABS alloy, unreinforced, heat stabilised |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.6 | % | ISO 294-4 |
| Flow direction | 1.4 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.4 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1850 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 50.0 | MPa | ISO 527-2 |
| Fracture | 43.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.5 | % | ISO 527-2 |
| Fracture | 70 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 19 | kJ/m² | ISO 179/1eA |
| 23°C | 85 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.00 mm) | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.10 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >70% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.14 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 245 - 270 | °C | |
| Middle Temperature | 260 - 275 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Processing (Melt) Temp | 265 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 50.0 | MPa | |
| Holding Pressure | 30.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH501G4 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| TECHNOGRAN® IONOMERE NAT CLEAR | Eurocompound Polymers | Ionomer | TECHNOGRAN® |
| Viton® GFLT-200S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Bergamid™ A70 H NC166 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Capran® 1200T | Honeywell | Nylon 6 | Capran® |