Estane® 2355-95AE TPU
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kWiOGH_Estane-2355-95AE-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
2355-95AE is a thermoplastic polyurethane elastomer. Feature: Fuel resistant, extrusion laminate coating |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 - 0.90 | % | ASTM D955 |
| Transverse flow | 0.60 - 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 94 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (3.20 mm) | 89.6 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 g, H-22 Wheel) | 4.00 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% strain, 3.20mm | 8.30 | MPa | ASTM D412 |
| 100% strain, 3.20mm | 9.70 | MPa | ASTM D412 |
| 300% strain, 3.20mm | 21.4 | MPa | ASTM D412 |
| Tensile Strength (Break, 3.20 mm) | 38.9 | MPa | ASTM D412 |
| Tensile Elongation (Break, 3.20 mm) | 450 | % | ASTM D412 |
| Tensile Elongation at Break (3.20 mm) | 60 | % | ASTM D412 |
| Tear Strength 1(3.20 mm) | 105 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 25°C, 22 hr | 30 | % | ASTM D395B |
| 70°C, 22 hr | 80 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -15.0 | °C | DSC |
| Vicat Softening Temperature | 80.6 | °C | ASTM D1525 2 |
| CLTE - Flow | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 - 104 | °C | |
| Mold Temperature | 16.0 - 60.0 | °C |
| Injection instructions |
|---|
| Air Dew Point: <-40°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 - 104 | °C | |
| Melt Temperature | 182 - 199 | °C |
| Extrusion instructions |
|---|
| Air Dew Point: <-40°C |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toughblend® PA66-1300 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| EVALENE® HDPE HB23551 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| Karina IVORY PVC COMPOUND -E 655-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Rnew® B522 | Altuglas International of Arkema Inc. | PLA+PMMA | Plexiglas® |
| Arnite® TV4 240-FC NA99001 | DSM Engineering Plastics | PBT | Arnite® |