Menzolit® SMC 0650
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kW8YCg_Menzolit-SMC-0650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 0650 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 0650 Low pressure SMC for large panels when moulding force becomes critical. Specific moulding pressure < 20 bar. A Special moulding procedure is necessary please. For details please contact your local Menzolit tech service team. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.15 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 50.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 7000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 133 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | Internal Method |
| Glass Transition Temperature | 170 | °C | DSC |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 95 | IEC 60707-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 120 to 150 | °C | |
| Injection Pressure | 1.00 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flontech® FT-905-RSC | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Emulprene® 10101A | INSA | SBR, Emulsion | Emulprene® |
| ORIENTENE FM 03 | Oriental Petrochemical Company | PP Homopolymer | ORIENTENE |
| Sylvin 8378-85 Orange 5112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OTECH TPE OTE6519 - A/V Jacket | OTECH Corporation | TPE | OTECH TPE |