Durethan® BC 304 000000

Category:	Nylon 6 , Polyamide 6
Manufacturer:	LANXESS GmbH
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kV0HdR_Durethan-BC-304-000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PA 6, non-reinforced, injection molding, improved impact strength

General Information
Features	Good Impact Resistance
Uses	Automotive Bumper Flexible Grips Luggage Rollers Sporting Goods
Agency Ratings	EC 1907/2006 (REACH)
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1)
Part Marking Code (ISO 11469)	ISO 1874-PA 6-HI, GR, 14-020

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity
--	1.05 1.06	--	g/cm³	ASTM D792
23°C	1.06	--	g/cm³	ISO 1183
Apparent Density	0.60	--	g/cm³	ISO 60
Molding Shrinkage				ISO 2577
Across Flow : 260°C, 3.00 mm ¹	1.5	--	%
Across Flow : 120°C, 4 hr, 3.00 mm ²	0.46	--	%
Flow : 260°C, 3.00 mm ³	1.1	--	%
Flow : 120°C, 4 hr, 3.00 mm ⁴	0.38	--	%
Water Absorption				ISO 62
Saturation, 23°C	7.5	--	%
Equilibrium, 23°C, 50% RH	2.2	--	%

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	80.0	35.0	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
23°C ⁵	1800	800	MPa	ASTM D638
23°C	1800	800	MPa	ISO 527-2/1
Tensile Strength (Yield, 23°C)	45.0	35.0	MPa	ASTM D638, ISO 527-2/50
Tensile Elongation
Yield, 23°C	4.0	--	%	ASTM D638
Yield, 23°C	4.5	30	%	ISO 527-2/50
Break, 23°C	> 200	> 200	%	ASTM D638
Nominal Tensile Strain at Break (23°C)	> 50	> 50	%	ISO 527-2/50
Flexural Modulus
23°C	1600	752	MPa	ASTM D790
23°C ⁶	1600	700	MPa	ISO 178/A
Flexural Strength
5.0% Strain, 23°C	55.2	31.0	MPa	ASTM D790
3.5% Strain, 23°C	55.0	25.0	MPa	ISO 178/A
23°C ⁷	60.0	30.0	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁸(23°C)	7.0	9.0	%	ISO 178/A

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behavior ⁹(> 1.00 mm)	passed	--		ISO 3795

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6-HI, GR, 14-020	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.030 to 0.12	%	Karl Fisher

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	20	20	kJ/m²
23°C	85	120	kJ/m²
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	No Break	No Break
23°C	No Break	No Break
Notched Izod Impact
-40°C, 3.18 mm	650	650	J/m	ASTM D256
23°C, 3.18 mm	650	920	J/m	ASTM D256
-30°C	30	17	kJ/m²	ISO 180/1A
23°C	70	100	kJ/m²	ISO 180/1A
Multi-Axial Instrumented Impact Energy				ISO 6603-2
-30°C	125	--	J
23°C	120	125	J

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed, 39.9 mm	90.0	--	°C	ASTM D648
0.45 MPa, Unannealed	90.0	--	°C	ISO 75-2/B
1.8 MPa, Unannealed	50.0	--	°C	ISO 75-2/A
1.8 MPa, Annealed, 3.99 mm	50.0	--	°C	ASTM D648
8.0 MPa, Unannealed	40.0	--	°C	ISO 75-2/C
Vicat Softening Temperature	150	--	°C	ISO 306/B50, ISO 306/B120
Ball Pressure Test (194°C)	Pass	--		IEC 60695-10-2
Melting Temperature ¹⁰	222	--	°C	ISO 11357-3
CLTE				ISO 11359-2
Flow : 23 to 55°C	1.5E-4	--	cm/cm/°C
Transverse : 23 to 55°C	1.6E-4	--	cm/cm/°C

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+14 to 1.0E+15	1.0E+13 to 1.0E+14	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+15	1.0E+12 to 1.0E+13	ohms·cm	IEC 60093
Electric Strength				IEC 60243-1
23°C, 1.00 mm	35	35	kV/mm
23°C, 3.00 mm	36	36	kV/mm
Dielectric Constant				IEC 60250
23°C, 50 Hz ¹¹	3.30	9.60
23°C, 1 MHz ¹²	3.10	3.50
23°C, 100 Hz	3.30	11.0
23°C, 1 MHz	3.00	3.50
Dissipation Factor				IEC 60250
23°C, 50 Hz	0.010	0.15
23°C, 100 Hz	7.0E-3	0.18
23°C, 1 MHz	0.010 0.015	0.060 0.090
Comparative Tracking Index
Solution A ¹³	600	--	V	IEC 60112
Solution B ¹⁴	600	--	V	IEC 60112
--	--	600	V	ASTM D3638

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.60 mm	HB	--
3.20 mm	HB	--
Glow Wire Flammability Index (2.00 mm)	650	--	°C	IEC 60695-2-12
Oxygen Index ¹⁵	21	--	%	ISO 4589-2

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 to 6.0	hr
Processing (Melt) Temp	260 to 280	°C
Mold Temperature	80.0 to 90.0	°C

Note Message
1 .	150x105x3mm, 80°C MT, 500 bar
2 .	150x105x3mm
3 .	150x105x3mm, 80°C MT, 500 bar
4 .	150x105x3mm
5 .	1.0 mm/min
6 .	2.0 mm/min
7 .	2.0 mm/min
8 .	2 mm/min
9 .	US-FMVSS302
10 .	10°C/min
11 .	Tinfoil Electrodes
12 .	Tinfoil Electrodes
13 .	Depth of Erosion: 1.70 mm
14 .	Depth of Erosion: 2.30 mm
15 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
Rigidex® P 450-HP90	INEOS Olefins & Polymers Europe	PP Impact Copolymer	Rigidex® P
RheTech Polypropylene F43-01B	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
Borealis PP HD244CF	Borealis AG	PP Homopolymer	Borealis PP
Huaxia Shenzhou FKM 246G	Shandong Huaxia Shenzhou New Material Co., Ltd.	Fluorelastomer	Huaxia Shenzhou
Panlite® L-1225LM	TEIJIN LIMITED	PC	Panlite®