Elastamax™ TM0200-0085 Black
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Elastamax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kUMEKf_Elastamax-TM0200-0085-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Elastamax™ XL thermoplastic olefins (TPOs) are based on pelletized blends of polyolefin resins and select elastomers such EPDM. These materials have been engineered to provide a balance of physical properties and processability, and are an economical alternative to traditional thermoset rubber and more costly thermoplastic elastomers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 15 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 89 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 9.65 | MPa | ASTM D412A |
| Tensile Elongation 2(Break) | 700 | % | ASTM D412A |
| Tear Strength 3 | 59.5 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 290 | J/m | ASTM D256 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | Die C, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® VK6 HIT1 NERO900 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| TAROLOX 10 K6 | Taro Plast S.p.A. | PBT | TAROLOX |
| NuSil MED-2014 | NuSil Technology | Silicone | NuSil |
| Durepol® PBT A3 G30 PRTA011 BT304 MSP | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| ELASTEL™ CR-FR-5 | HELLENIC CABLES S.A. | PCR | ELASTEL™ |