Order Products : sales@su-jiao.com
OmniPro™ HPP CCF10
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniPro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kTnPM1_OmniPro-HPP-CCF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% CaCO 3 Reinforced, Homopolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1590 | MPa | ASTM D790 |
| Flexural Strength | 44.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 104 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 60.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 216 to 260 | °C | |
| Nozzle Temperature | 216 to 260 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AG15A1 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Karina IVORY PVC COMPOUND 650D35/ 1-C-ISI-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PETOPLEN EH 102 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |
| Polifor® 5020/V2 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| GELOY™ CR8510 resin | SABIC Innovative Plastics | ASA | GELOY™ |