LNP VERTON UV00AS is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* VERTON* Compound UF-700-10 HS Product reorder name: UV00AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.67 | g/cm³ | ASTM D792 |
| -- | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.48 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.20 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19300 | MPa | ASTM D638 |
| -- | 19200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 258 | MPa | ASTM D638 |
| Yield | 222 | MPa | ISO 527-2 |
| Fracture | 258 | MPa | ASTM D638 |
| Fracture | 222 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.8 | % | ASTM D638 |
| Yield | 1.4 | % | ISO 527-2 |
| Fracture | 1.8 | % | ASTM D638 |
| Fracture | 1.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 17200 | MPa | ASTM D790 |
| -- | 17000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 386 | MPa | ASTM D790 |
| -- | 393 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D256 |
| 23°C 2 | 42 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 78 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.90 | J | ASTM D3763 |
| -- | 7.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 291 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 296 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 266 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 272 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN SFO-130A | Lotte Chemical Corporation | PP Homopolymer | RANPELEN |
| Unichem 5433 | Colorite Polymers | PVC, Unspecified | Unichem |
| Next Nylon 6 Prime Series NG30-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Generic TPU-Ester/Ether | Generic | TPU-Ester/Ether | Generic |
| Sylvin 7833-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |