TECHNYL® A 218 V35 Y10 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kTHbch_TECHNYLA218V35Y10NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218 V35 Y10 Natural is a polyamide 66, reinforced with 35% of glass fiber, heat stabilized and specially modified to have improved frictionnal properties, for injection moulding. This grade offers an excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183/A |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.65 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12700 | 8700 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield, 23°C | 185 | 128 | MPa | ASTM D638 |
| Fracture, 23°C | 204 | 133 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Fracture, 23°C | 2.7 | 5.5 | % | ASTM D638 |
| Fracture, 23°C | 2.6 | 5.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 72 | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 11 | 13 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 80.0 | 100 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 60 | 75 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 262 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 275 - 285 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Mold Temperature | 70 - 100 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB1411 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| NEXUS PS 830 | Nexus Resin Group, LLC. | PS (HIPS) | NEXUS PS |
| Axiall PVC 17900 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| EVERLON® TY-60 | Ever Polymer Co., Ltd. | SBS | EVERLON® |
| GPP™ 1020 | S&E Specialty Polymers, LLC | TPO (POE) | GPP™ |