Synthos PS HI 662E
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kTFnBi_Synthos-PS-HI-662E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SYNTHOS PS HI 662E is high-impact polystyrene (HIPS) with matt appearance and properties that are suitable for thermoforming. It is a thermoplastic material designed for extrusion and thermoforming. Product has a form of lens granules of diameter 2.5 to 4 mms. APPLICATION Extrusion is used to produce visually demanding sheets and plates which are then thermoformed to packaging, technical parts or other consumer and industrial articles. The composition of the polymer meets the requirements of the Health and can therefore be used for the production of articles coming into contact with food. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 to 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.60 | % | Internal Method |
| Particle Size | 2.50 to 4.00 | mm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Styrene | 0.025 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 150 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Desiccant Dryer | 80.0 | °C | |
| Hot Air Dryer | 70.0 | °C | |
| Drying Time | |||
| Desiccant Dryer | 1.0 | hr | |
| Hot Air Dryer | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 270 | °C | |
| Mold Temperature | 10.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® G natural | Röchling Engineering Plastics SE & Co. KG | HDPE | POLYSTONE® |
| TPV Elastoprene® N67A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| ALTECH® PA6 B 2030/500 GF30 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Chemical Resources PP 3000BF | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| Plaslube® PA6 GF30 RM BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |