OmniCarb™ PC/PBT 1420 CTI
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kRT1go_OmniCarb-PC-PBT-1420-CTI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cold Temperature Impact Resistant, PC/PBT |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 2140 | MPa | ASTM D790 |
| Flexural Strength | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 530 | J/m | |
| 23°C, 3.18 mm | 740 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 104 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 93.3 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 249 to 282 | °C | |
| Front Temperature | 249 to 282 | °C | |
| Nozzle Temperature | 249 to 282 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITAL® H BK | Nytef Plastics, Ltd. | Acetal (POM) Homopolymer | UNITAL® |
| CP PRYME® Polycarbonate PC100RUL-10M BK | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| FMC® 201 | Smooth-On, Inc | Polysulfide Rubber | FMC® |
| Haysite Plastics HCR-100 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| SABIC® PPcompound 9125 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |