TRIBOCOMP® PEEK TS9
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kRIbSr_TRIBOCOMP-PEEK-TS9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PEEK TS9 is a polyetheretherketone (PEEK) product,. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.1 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.14 | ASTM D3702 | |
| Static | 0.12 | ASTM D3702 | |
| Wear Factor | 8.00 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 65 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 300 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 175 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 4.5E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.50 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 340 - 360 | °C | |
| Middle Temperature | 360 - 380 | °C | |
| Front Temperature | 380 - 390 | °C | |
| Nozzle Temperature | 380 - 390 | °C | |
| Mold Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPV Elastoprene® N90A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Network Polymers HDPE 50 0863 | Network Polymers, Inc. | HDPE | Network Polymers HDPE |
| APEX® 1500-85D | Teknor Apex Company | PVC, Flexible | APEX® |
| Delrin® 300PE BK602 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| POLYfill PP CV8030 LR UV | Polykemi AB | PP, Unspecified | POLYfill |