NYCOA Polyamide 471
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kRCiQn_NYCOA-Polyamide-471.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 471 is a medium viscosity Nylon 6 resin particularly suitable for extrusion processing. It possesses an excellent combination of strength, and toughness; as well as excellent heat, chemical, and abrasion resistance inherent to Nylon 6. Its high melt viscosity and strength provide ease of processing from either a flat or a circular die. Similarly, tubes, pipes, and tapes have been processed with excellent results. Injection molding of high strength parts can be accomplished with molding cycles similar to those obtained with general purpose grade resins, even though higher cylinder temperatures may sometimes be required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 2.6 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 1.6 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus 3 | 250 | MPa | ASTM D790 |
| Flexural Strength 4 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 177 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| Relative Viscosity, NYCOA method: 3.3 to 3.5 SAVWater Extractable, NYCOA method: Max 0.8%Melt Mass- Flow Rate (MFR). ASTM D1238, 235°C/1.0kg: 2.4 to 2.8 g/10minTensile Elongation at Break, ASTM D638, 2 in/min: 100+%The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3935T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sinvicomp SGH8000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Daelim Po1y® LH-4100 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Geon™ Vinyl Rigid Molding 85891 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| Moplen RP398V | LyondellBasell Industries | PP Random Copolymer | Moplen |