MAJORIS AFR090 - 8229
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kQcfGd_MAJORIS-AFR090---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AFR090 - 8229 is a halogen flame retardant compound UL 94 V0, intended for blow moulding extrusion and profiles. APPLICATIONS AFR090 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts (conform 2002/95/EC, RoHS directive).
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 815 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1130 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 69 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 190 | °C | |
| Cylinder Zone 3 Temp. | 180 to 190 | °C | |
| Cylinder Zone 5 Temp. | 180 to 190 | °C | |
| Melt Temperature | 200 | °C | |
| Head Temperature | 200 | °C | |
| Die Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPH4TF-2 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Nanjing Hongrui PA66 A830 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| BMC T15(GP) | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Braskem PE LL 5800 N | Braskem | LLDPE | Braskem PE |
| DAI-EL™ G-558 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |