Infino HN-3102G
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kQ1AKx_Infino-HN-3102G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HN-3102G is a Polycarbonate (PC) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 | g/cm³ | ASTM D792 |
| -- | 1.27 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/10.0 kg | 33 | g/10 min | ASTM D1238 |
| 250°C/10.0 kg | 31 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.40 | % | ASTM D955 |
| Ash Content | 10 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3200 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 84.0 | MPa | ASTM D638 |
| Yield | 75.0 | MPa | ISO 527-2/5 |
| Break 3 | 64.0 | MPa | ASTM D638 |
| Break | 69.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 5.2 | % | ASTM D638 |
| Break | 5.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 4000 | MPa | ASTM D790 |
| -- 6 | 3700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 150 | MPa | ASTM D790 |
| -- 8 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 5.9 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 55 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 49 | J/m | ASTM D256 |
| 23°C 10 | 5.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 142 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 132 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ISO 306/B50 |
| -- | 146 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 1.60 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 260 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 93.2 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 182 HEC | RTP Company | PP, Unspecified | RTP |
| Radilon® A ERV1003LK 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| SLOVASTER® B GF 40 | Plastcom | PBT | SLOVASTER® |
| FERREX® GPP20CC | Ferro Corporation | PP, Unspecified | FERREX® |
| Sumikon® PM-6600 | SBHPP | Phenolic | Sumikon® |