LUVOCOM®19-8939 is a polyamide 46 (nylon 46) material containing a carbon fiber reinforced material. This product is available in Europe,. LUVOCOM®The main features of 19-8939 are: Conductivity Electrostatic protection anti-warping Good stiffness Impact resistance Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Features	Conductivity Low warpage Rigid, good Electrostatic discharge protection Impact resistance, good Good strength
Uses	Gear Textile applications Engineering accessories Application in Automobile Field Business equipment Cam
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.21	g/cm³	ISO 1183
Molding Shrinkage	0.30 - 0.70	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	9000	MPa	ISO 527-2
Tensile Stress (Break)	130	MPa	ISO 527-2
Tensile Strain (Yield)	4.8	%	ISO 527-2
Flexural Modulus	7500	MPa	ISO 178
Flexural Stress	190	MPa	ISO 178
Flexural Strain at Flexural Strength	6.2	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	160	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+8	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength
-30°C	65	kJ/m²	ISO 179/1fU
23°C	72	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	150	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+8	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
A	80.0	°C
Vacuum dryer, B	80.0	°C
Drying Time
A	2.0 - 8.0	hr
Vacuum dryer, B	2.0 - 12	hr
Suggested Max Moisture	0.10	%
Rear Temperature	285 - 315	°C
Middle Temperature	305 - 315	°C
Front Temperature	305 - 315	°C
Nozzle Temperature	280 - 330	°C
Processing (Melt) Temp	310	°C
Mold Temperature	120 - 140	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 46 , Polyamide 46
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kPE6Rs_LUVOCOM-19-8939.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
AKROMID® B3 GF 30 1 natural (2464)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
Axiall PVC 1901 Clear 7002	Axiall Corporation	PVC, Flexible	Axiall PVC
Durolon® IR2000 CR010	Unigel Plásticos	PC	Durolon®
Jamplast Ex-02 ABS	Jamplast, Inc.	ABS	Jamplast
ALCUDIA® LDPE CP-121	REPSOL	LDPE	ALCUDIA® LDPE