FERREX® GPP35CF UL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kOhmnF_FERREX-GPP35CF-UL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERREX®GPP35CF UL is a polypropylene material, which contains 36% calcium carbonate filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. FERREX®The main features of GPP35CF UL are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 - 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 37.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D256 |
| Dart Drop Impact (3.18 mm) | 14.7 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 98.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 199 - 204 | °C | |
| Middle Temperature | 204 - 210 | °C | |
| Front Temperature | 210 - 216 | °C | |
| Nozzle Temperature | 216 - 221 | °C | |
| Mold Temperature | 46.1 - 60.0 | °C | |
| Back Pressure | 0.138 - 0.345 | MPa | |
| Screw Speed | 100 - 150 | rpm | |
| Clamp Tonnage | 2.8 - 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 218L V30 BLACK Z/4 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| ULTZEX™ 25100J | Prime Polymer Co., Ltd. | LLDPE | ULTZEX™ |
| DOW™ LDPE PG 7004 (Injection Molding) | The Dow Chemical Company | LDPE | DOW™ LDPE |
| GERMAMID 6 GF 10 H | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| Starex VE-0860 P | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |