Order Products : sales@su-jiao.com
TAIRILAC AX4100
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRILAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kNc8oL_TAIRILAC-AX4100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC ABS resin AX4100 meets the requirements of UL, SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class R, 23°C | 107 | ASTM D785 | |
| R scale, 23°C | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 39.2 | MPa | ASTM D638 |
| 23°C | 39.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2350 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 69.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 140 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648, ISO 75-2/A | ||
| 1.8 MPa, unannealed, 12.7mm | 106 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, annealed 1 | 116 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/A, ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 95.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Mold Temperature | 40.0 - 90.0 | °C | |
| Injection Pressure | 68.6 - 118 | MPa |
| Injection instructions |
|---|
| Screw Temp: 200 to 250°C |
| Note Message | |
|---|---|
| 1 . | 95°Cx8Hr |
| 2 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam AFR430B1 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Carbotex K-40UV | Kotec Corporation | PC | Carbotex |
| Karina CREPE PVC COMPOUND 870-22/70-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kareline® PLMS7525 | Plasthill Oy | PLA | Kareline® |
| Sylvin 3200-60 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |