Moplen RP310M is a slightly modified propylene random copolymer for manufacturing high transparent cast films. It contains no slip or antiblocking agents. It offers excellent processability, high clarity and gloss and good heat weldability. Main applications are packaging of foodstuffs, packaging of books and stationary. Moplen RP310M is suitable for food contact. For regulatory information please refer to Moplen RP310M Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 11 | % | |
| Break | 520 | % | |
| Coefficient of Friction | DIN 53375 | ||
| vs. Itself - Dynamic | > 0.50 | ||
| vs. Itself - Static | > 0.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD 1(50 µm) | 780 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 50 µm | 20.0 | MPa | |
| Break, 50 µm | 40.0 | MPa | |
| Tensile Elongation - MD 3 | ASTM D882 | ||
| Yield, 50 µm | 6.3 | % | |
| Break, 50 µm | 730 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 1.4 | kJ/m² | |
| 23°C | 3.4 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 72.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 139 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 91 | ASTM D2457 | |
| Haze (50.0 µm) | < 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide AR-36 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Grilamid® TR 90 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Karina CLEAR PVC COMPOUND -E 65/200-D | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPH K8040 | Polykemi AB | PP Homopolymer | POLYfill |
| CYCOLAC™ MG38F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |