Laril 13-V1KC
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laril |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kMrbUN_Laril-13-V1KC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified Polyphenylene Oxyde (PPOm). Product UL certified. High dimensional stability. Good thermal resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.40 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 5000 | MPa | |
| 60°C | 4300 | MPa | |
| 90°C | 3600 | MPa | |
| 120°C | 3200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 120°C | 20.0 | MPa | |
| Break, 23°C | 65.0 | MPa | |
| Break, 60°C | 55.0 | MPa | |
| Break, 90°C | 40.0 | MPa | |
| Break, 120°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 120°C | 1.5 | % | |
| Break, 23°C | 2.0 | % | |
| Break, 60°C | 2.0 | % | |
| Break, 90°C | 2.2 | % | |
| Break, 120°C | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 105 | °C | |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 5.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-1 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE LLB1918F | Trademark Plastics Corporation | LLDPE | Trademark PE |
| TOTAL Polyethylene HDPE XS 10 OS | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| AKROMID® T1 GF 30 9 black (3498) | AKRO-PLASTIC GmbH | PPA | AKROMID® |
| APEX® 85-J438D-8 | Teknor Apex Company | PVC, Flexible | APEX® |
| Petrotene® PP A3 AE BRC0001 PH312 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |