MEGOLON™ HF 8553 NATURAL
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kMesm8_MEGOLON-HF-8553-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A FLEXIBLE, THERMOPLASTIC, ZERO HALOGEN, FLAME RETARDED OLEFINIC JACKETING COMPOUND INTENDED FOR DEMANDING TELECOMMUNICATION CABLES (IEC 332-3C, CMR). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 to 1.63 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D | 54 to 60 | ||
| Shore D, 15 sec | 44 to 50 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 10.3 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 150 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1 | UL Unspecified | ||
| 121°C, 168 hr | 6.0 | % | |
| 136°C, 168 hr | 8.0 | % | |
| Change in Ultimate Elongation in Air 2 | UL Unspecified | ||
| 121°C, 168 hr | -2.0 | % | |
| 136°C, 168 hr | -4.0 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -16.0 | °C | ASTM D746 |
| Hot Pressure Test - % Loss (80°C) | 25 | % | IEC 811-3-1 |
| Temperature Index | 315 | °C | NES 715 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission Conductivity | 0.462 | µS/mm | IEC 60754-2 |
| Acid Gas Emission pH | |||
| -- | 5.40 | IEC 60754-2 | |
| -- | 3.42 | MIL C-24643 | |
| Halogen Content | |||
| -- | < 5 | mg/g | IEC 60754-1 |
| -- | 0 | % | MIL C-24643 |
| NBS Smoke Density | ASTM E662 | ||
| Flaming, Dmc : 3.18 mm | 250 | ||
| Non-Flaming, Dmc : 3.18 mm | 140 | ||
| Smoke Index | 3.00 | NES 711 | |
| Toxicity | 4.30 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission | 0.35 | % | MIL C-24643 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Draw Down | 1.5:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant | ASTM D150 | ||
| 23°C, 1 MHz | 3.88 | ||
| 23°C, 100 MHz | 3.87 | ||
| 23°C, 350 MHz | 3.75 | ||
| 23°C, 1.00 GHz | 3.19 | ||
| Dissipation Factor | ASTM D150 | ||
| 23°C, 1 MHz | 0.022 | ||
| 23°C, 100 MHz | 0.015 | ||
| 23°C, 350 MHz | 6.8E-3 | ||
| 23°C, 1.00 GHz | 1.1E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 48 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 to 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | Thickness: 30 mil |
| 2 . | Thickness: 30 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecolen® CP30 NL XA80 | Eurotec Engineering Plastics | PP Copolymer | Tecolen® |
| CoolPoly® D5108 | Celanese Corporation | PPS | CoolPoly® |
| Daelim Po1y® TR-418YL | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| DOMAMID® 6AF | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| ADENE® O05XQB-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |