SURPASS® HPs019-F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SURPASS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kKnsFG_SURPASSHPs019F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SURPASS®HPs019-F is a linear low density polyethylene material,. This product is available in North America and is processed by film extrusion. SURPASS®The main features of the HPs019-F are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 76 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 165 | MPa | ASTM D882 |
| 1% sectioning, MD : 76 µm, blown film | 180 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 175 | MPa | ASTM D882 |
| 1% sectioning, TD : 76 µm, blown film | 200 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 9.50 | MPa | ASTM D882 |
| MD : yield, 76 µm, blow film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 9.80 | MPa | ASTM D882 |
| TD : yield, 76 µm, blow film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 49.0 | MPa | ASTM D882 |
| MD : broken, 76 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : broken, 76 µm, blown film | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 520 | % | ASTM D882 |
| MD : broken, 76 µm, blown film | 720 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| TD : broken, 76 µm, blown film | 820 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709A | ||
| 25 µm, blown film | 480 | g | ASTM D1709A |
| 76 µm, blown film | 1000 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 280 | g | ASTM D1922 |
| MD : 76 µm, blown film | 1100 | g | ASTM D1922 |
| TD : 25 µm, blown film | 470 | g | ASTM D1922 |
| TD : 76 µm, blown film | 1400 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45, 25.0 µm, blown film | 35 | ASTM D2457 | |
| 45 °, 76.2 µm, blown film | 40 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25.0 µm, blown film | 22 | % | ASTM D1003 |
| 76.2 µm, blown film | 23 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture 1 | Internal method | ||
| 25.0 µm | 550 | J/cm | Internal method |
| 76.2 µm | 450 | J/cm | Internal method |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 5013S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Colorite G Series 6012G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| Generic Acetal (POM) Copolymer+PE | Generic | Acetal (POM) Copolymer+PE | Generic |
| Huafon JF-P-4170T / JF-I-4118 (outsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| LOTTMER HX-086AB | Lotte Chemical Corporation | TPE | LOTTMER |