Nylfor® 74S5251PO 0001
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nylfor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kKYpBA_Nylfor-74S5251PO-0001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard viscosity polyamide 66, 25% glass fiber reiforced. Flame retardant grade UL94V-0 with red phosphorous |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 5.5 | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 150 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 7800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3485-4 | RTP Company | LCP | RTP |
| RMA 160 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| Lion Idemitsu Composites PPS G141Z1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| LG ABS PI642G | LG Chem Ltd. | ABS | LG ABS |
| Petrothene® NA206000 (Extrusion Coating) | LyondellBasell Industries | LDPE | Petrothene® |