Michimid K4200GF33-03
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michimid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kKRGR4_Michimid-K4200GF33-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michimid K4200GF33-03 is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 7590 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 246 | °C | |
| 1.8 MPa, Unannealed | 227 | °C | |
| Melting Temperature | 265 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 293 | °C | |
| Middle Temperature | 288 | °C | |
| Front Temperature | 288 | °C | |
| Nozzle Temperature | 282 | °C | |
| Processing (Melt) Temp | 288 | °C | |
| Mold Temperature | 65.6 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LD02023 - CM | Premier Polymers, LLC. | LDPE | Premier |
| PRIME TPO F-3900H | Prime Polymer Co., Ltd. | PP Homopolymer | PRIME TPO |
| Telcar® TL-2519F | Teknor Apex Company | TPE | Telcar® |
| COSMOPLENE® FL7013E2 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Homopolymer | COSMOPLENE® |
| Polimid B 30 GF V0HFR KW | Poliblend S.p.a. | Nylon 6 | Polimid B |