Badamid® LB70 GF30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kKL6QU_Badamid-LB70-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass fibres rinforced injection moulding grade for technical and electrical isolating products |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.3 to 6.9 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 to 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 9500 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 190 | 115 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 3.5 | 8.0 | % | ISO 527-2/5 |
| Flexural Stress 4(23°C) | 270 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 15 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 16 | 20 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 5 | 222 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 2.0E-5 to 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 to 7.0E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 60216 | |||
| -- 6 | 135 | -- | °C | |
| -- | 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | 6.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.023 | 0.22 | IEC 60250 | |
| Comparative Tracking Index | 575 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 10 K/min |
| 6 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2266 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Nanjing Hongrui PP P353 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Enviramid® N2325HL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| POLYfill PP HIP8040 VT2 | Polykemi AB | PP, Unspecified | POLYfill |
| POLYFLAM® RPP 1275 | A. Schulman Europe | PP Homopolymer | POLYFLAM® |