Nirion 3550/M
| Category: | PC , Polycarbonate |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Nirion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kKF9M9_Nirion-3550-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate for injection moulding, suitablo for general purpose, very high MFI and good impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 43 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 65 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 2400 | MPa | ASTM D790 |
| Flexural Strength 2(Break) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 50 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 122 | °C | ASTM D648 |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 3 |
| CLTE - Flow (23 to 55°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Melt Mass- Flow Rate (MFR), ASTM D1238, 300°C/1.2kg: 35 to 50 g/10min |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx F663E13 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| Reny® 1371 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Trademark PE LLD2920G | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Amilan® CM3001G-45 | Toray Resin Company | Nylon 66 | Amilan® |
| Thermec N™ 4314R25T1H | Technical Polymers, LLC | PPA | Thermec N™ |